卷 51, 期 5, 页码 1172-1180出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2009.02.027
关键词
Metal coatings; Nickel; SEM; High temperature corrosion; Oxidation
资金
- Material Performance Technologies
- The University of Auckland
Composites of Cr3C2-NiCr provide superior oxidation resistance to WC-Co composites, which has seen them applied extensively to components subjected to combined high temperature erosion and oxidation. This work characterises the variation in oxidation mechanism of thermally sprayed Cr3C2-NiCr composites at 700 degrees C and 850 degrees C as a function of heat treatment. Carbide dissolution during spraying increased the Ni alloy Cr concentration, minimising the formation of Ni oxides during oxidation. Compressive growth stresses resulted in ballooning of the oxide over the carbide grains. Carbide nucleation with heat treatment reduced the Ni alloy Cr concentration. The oxidation mechanism of the composite coating changed from being Cr based to that observed for NiCr alloys. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据