CORROSION SCIENCE
卷 50, 期 12, 页码 3569-3575出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2008.09.008
关键词
Aluminum; EIS; SEM; Oxide coatings
资金
- Lam Research Corporation
The corrosion resistance of anodized AI 6061 produced by two different anodizing and sealing processes was evaluated using electrochemical impedance spectroscopy (EIS). The scanning electron microscope (SEM) was employed to determine the surface structure and the thickness of the anodized layers. The EIS data revealed that there was very little change of the properties of the anodized layers for samples that were hard anodized in a mixed acid solution and sealed in hot water over a 365 day exposure period in a 3.5 wt% NaCl solution. The specific admittance AS and the breakpoint frequency f(b) remained constant with exposure time confirming that the hard anodizing process used in this study was very effective in providing excellent corrosion resistance of anodized AI 6061 over extended exposure periods. Some minor degradation of the protective properties of the anodized layers was observed for samples that were hard anodized in H2SO4 and exposed to the NaCl solution for 14 days. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据