期刊
CORROSION SCIENCE
卷 50, 期 3, 页码 847-855出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2007.09.004
关键词
superalloys; metal coatings; potentiostatic; atmospheric corrosion; pitting corrosion
NiCoCrAlYSiB coatings were deposited by arc ion plating (AIP) and annealed/pre-oxidised under various conditions. The corrosion behaviour of as-deposited and annealed/pre-oxidised coatings was studied by salt spray testing in a neutral mist of 5 wt% NaCL at 35 degrees C for 200 h. The results showed that the as-deposited NiCoCrAlYSiB coating behaved poorly while the annealed and pre-oxidised ones performed much better in salt spray tests. The dense microstructure in annealed coatings and formation of alpha-Al2O3 scales on the surface during pre-oxidation improved the corrosion resistance in salt spray test. The corrosion process was investigated from the aspects of corrosion products, and its electrochemical mechanism was proposed as well. (C) 2007 Elsevier Ltd. All rights reserved.