CONSTRUCTION AND BUILDING MATERIALS
卷 187, 期 -, 页码 318-326出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2018.07.220
关键词
Coal gangue geopolymer; XRD analysis; TG-DTG analysis; SEM; Compressive strength
资金
- National Natural Science Foundation of China (NSFC) [51578539]
- Beijing Natural Science Foundation [8164061]
- Open Research Project of State Key Laboratory of Coal Resources and Safe Mining, China University of Mining and Technology [SKLCRSM16KFD07]
This paper explores the impacts of sodium hydroxide modulus, alkali lye amount and liquid-solid ratio on the strength and microstructure of coal gangue geopolymer materials, involving a total of five sodium hydroxide moduli, four NH/NS mass ratios and seven liquid-solid ratios. To characterize the morphology and structure of coal gangue geopolymer materials, we carried out XRD, TG-DTG, FT-IR and SEM analysis on the specimens respectively. The results show that NH concentration has no impact on paste fluidity and has significant impact on compressive strength of geopolymers. Both paste fluidity and compressive strength of geopolymers increase with the increase in liquid-solid ratio. However, it should be noted that the compressive strength decreases with the increase in liquid-solid ratio when the liquid-solid ratio is greater than 0.32. The optimal NH/NS mass ratio is 1:1.5 similar to 1:2. In comparison with P.O42.5 cement specimens, coal gangue geopolymers have higher initial strength and lower 28 d compressive strength. The analytical results of microstructure are consistent with those of compressive strength, which demonstrates that the polymerization products of coal gangue geopolymers are N-A-S-H gels and some other aluminosilicate zeolite crystals. (C) 2018 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据