CONSTRUCTION AND BUILDING MATERIALS
卷 23, 期 5, 页码 1855-1861出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2008.09.023
关键词
High-performance concrete; Permeability; Polypropylene fibres; Strength; Temperature; Thermal gradient
Permeability is one of the most important parameters to quantify the durability of high-performance concrete. Permeability is closely related with the spalling phenomenon in concrete at elevated temperature. This parameter is commonly measured on non-thermally damaged specimens. This paper presents the results of an experimental investigation carried out to study the effect of elevated temperature on the permeability of high-performance concrete. For this purpose, three types of concrete mixtures were prepared: (i) control high-performance concrete; (ii) high-performance concrete incorporating polypropylene fibres; and (iii) high-performance concrete made with lightweight aggregates. A heating-cooling cycle was applied on 160 x 320 mm, 110 x 220 mm, and 150 x 300 mm cylindrical specimens. The maximum test temperature was kept as either 200 or 600 degrees C. After the thermal treatment, 65 mm thick slices were cut from each cylinder and dried prior to being subjected to permeability test. Results of thermal gradients in the concrete specimens during the heating-cooling cycles, compressive strength, and splitting tensile strength of concrete mixtures are also presented here. A relationship between the thermal damage indicators and permeability is presented. (c) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据