期刊
COMPOSITES SCIENCE AND TECHNOLOGY
卷 89, 期 -, 页码 52-60出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compscitech.2013.09.018
关键词
Polymer-matrix composites (PMCs); Nanoparticles; Mechanical properties
资金
- Program for New Century Excellent Talents in University, People's Republic of China
SiO2 nanoparticles without surface modification were used to prepare a polymer based nanocomposite: methyl methacrylate (MMA) was selected as the matrix, and copolymerized with a small amount of cationic functional comonomer 2-(methacryloyloxy)ethyltrimethylammonium chloride (MTC). The aim is to improve the dispersion of unmodified SiO2 as well as the interfacial adhesion through electrostatic interaction between the positively charged copolymer matrix and negatively charged fillers, and ultimately to improve the mechanical properties. The chemical structure of P(MMA-co-MTC)/SiO2 was characterized by H-1 nuclear magnetic resonance (H-1 NMR). The interaction between copolymer matrix and SiO2 nanoparticles was investigated by zeta potential and Fourier transform infrared spectroscopy (FT-IR). Meanwhile, the morphologies of the synthesized microspheres were studied by scanning electron microscopy (SEM) and the dispersion of SiO2 nanoparticles in P(MMA-co-MTC)/SiO2 was observed by transmission electron microscopy (TEM). Finally, the mechanical properties of P(MMA-co-MTC)/SiO2 was studied in detail and the tensile fracture surface was studied by SEM. The results indicate that, P(MMA-co-MTC)/SiO2 has been successfully synthesized by in situ suspension copolymerization, and the mechanical properties, especially the flexural property, were remarkably improved due to the better dispersion state and stronger interfacial adhesion ameliorated through electrostatic interaction. When the content of MTC and SiO2 is 10 wt% and 1.0 wt%, respectively, the optimal mechanical properties were obtained: compared to PMMA, the tensile strength was increased by 20.7% and the flexural strength was improved by as much as 140.7%. The whole process does not need surface modification, which makes this method more convenient and less costly. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据