Strain-rate-dependent failure criteria for composites

The objective of this study was to characterize the quasi-static and dynamic behavior of composite materials and develop/expand failure theories to describe static and dynamic failure under multi-axial states of stress. A unidirectional carbon/epoxy material was investigated. Multi-axial experiments were conducted at three strain rates, quasi-static, intermediate and high, 10(-4),1 and 180-400 s(-1), respectively, using off-axis specimens to produce stress states combining transverse normal and in-plane shear stresses. A Hopkinson bar apparatus and off-axis specimens loaded in this system were used for multi-axial characterization of the material at high strain rates. Stress-strain curves were obtained at the three strain rates mentioned. The measured strengths were evaluated based on classical failure criteria, (maximum stress, maximum strain, Tsai-Hill, Tsai-Wu, and failure mode based and partially interactive criteria (Hashin-Rotem, Sun, and Daniel). The latter (NU theory) is primarily applicable to interfiber/interlaminar failure for stress states including transverse normal and in-plane shear stresses. The NU theory was expressed in terms of three subcriteria and presented as a single normalized (master) failure envelope including strain rate effects. The NU theory was shown to be in excellent agreement with experimental results. (C) 2010 Elsevier Ltd. All rights reserved.