Polypropylene; Nanocomposites; PP-g-AA compatibilizer; Morphology; Permeability
资金
- CAPES
This work dealt with the morphology and permeability properties of polypropylene/organoclay nanocomposites prepared using an acrylic acid grafted polypropylene (PP-g-AA) as compatibilizing agent. Two PP-g-AA containing the same acrylic acid content (6 wt.%) and having different molar masses were tested. The o-MMT content was 0, 1 or 5 wt.% and the PP-g-AA/o-MMT mass ratio was 0/1, 1/1, 2/1 or 5/1. Results of wide angle X-ray scattering (WAXS) and transmission electron microscopy (TEM) showed that without the PP-g-AA, the o-MMT was dispersed in the PP/o-MMT in a micrometer scale, similar to a conventional microcomposite. With the PP-g-AA, the o-MMT was much better dispersed and its interlayers were intercalated and partly exfoliated by the polymer chains. CO2 permeability values decreased for all samples with the incorporation of the organoclay. The compatibilized samples showed a more significant reduction in CO2 permeability, up to 50% when compared to the neat PP. In general, the PP-g-AA acted satisfactorily in compatibilizing PP/organoclay nanocomposites. Moreover, samples prepared with the compatibilizer/organoclay ratio of 5/1 had better barrier properties. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据