COMPOSITES SCIENCE AND TECHNOLOGY
卷 68, 期 3-4, 页码 987-994出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compscitech.2007.07.010
关键词
carbon fiber; polymer-matrix composite; nanofibrous membrane; fracture toughness; microstructure
A novel approach for toughening carbon fiber/epoxy composite using electrospun polysulfone (PSF) nanofibrous membranes was performed. As-received membranes were composed of nanofibers with random orientation, and were directly electrospun onto layers of carbon fiber/epoxy prepregs to toughen the composites. According to the random dispersed nanofibers in the membranes, the inhornogeneous phase separation of polysulfone, which was generated in situ along the nanofibers direction during the curing of epoxy matrix, was proposed. Owing to the aligned PSF spheres, excellent mechanical properties of composites were obtained. Mode I interlaminar fracture toughness (G(IC)) increased 158%, 261% and 28 No by loading 1 wt%, 3 wt% and 5 wt% nanofibrous membranes, which was far higher than those of the same content PSF films toughened composites. DMTA tests revealed good compatibility between nanofibrous membranes and epoxy matrix. And the flexural properties increased slightly compared to untoughened composite. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据