Physical, mechanical and morphological properties of polymer composites manufactured from carbon nanotubes and wood flour

The objective of this investigation was to evaluate physical, mechanical and morphological properties of experimental polymer type panels made from single-wall carbon nanotube (SWCNT) and wood flour. The composites with different SWCNTs (0,1,2,3 phc) and maleic anhydride grafted polyethylene (MAPE) (0 and 3 phc) contents were mixed by melt compounding in an internal mixer and then the composites manufactured by injection molding method. The mass ratio of the wood flour to LOPE was 50/50 (w/w) in all compounds. Water absorption, thickness swelling, bending characteristics, impact strength and morphological properties of the manufactured composites were evaluated. Based on the findings in this work the water absorption and thickness swelling of the nanocomposites decreased with increasing with amount of the SWCNTs (from 1 to 3 phc) and MAPE (3 phc) in the panels. The mechanical properties of LDPE/wood-flour composites could be significantly enhanced with increased percentage of MAPE and SWCNTs content. Panels having 2 phc SWCNTs and 3 phc MAPE exhibited the highest impact strength value. Also Scanning Electron Microscope (SEM) micrographs showed that carbon nanotubes can fill the voids of wood plastic composites as well as addition of MAPE and SWCNTs enhanced interaction between the components. (C) 2012 Elsevier Ltd. All rights reserved.