Strain-rate effects on fracture behavior of unidirectional composite materials are studied. Single-edge notched multi-layered unidirectional graphite composites (T800/3900-2) are investigated to examine fracture responses under static and dynamic loading conditions using a digital speckle correlation method. The fracture parameters for growing cracks are extracted as a function of fiber orientation. A 20 digital image correlation (DIC) method is used to obtain time-resolved full-field in-plane surface displacements when specimens are subjected to quasi-static and impact loading. Stress intensity factor and crack extension histories for pure mode-I and mixed mode cases are extracted from the full-field displacements. When compared to the dynamic stress intensity factors at crack initiation, the static values are found to be consistently lower. The stress intensity factor histories exhibit a monotonic reduction under dynamic loading conditions whereas an increasing trend is seen after crack initiation under quasi-static loading cases. This is potentially due to dominant crack face fiber bridging effects in the latter cases. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据