Metal-matrix composites (MMCs); Microstructures; Mechanical properties; Sintering; Metallic glasses
资金
- French National [ANR-BLAN-06-035]
- World Premier Institute (WPI-Tohoku)
- National Basic Research Program of China [2007CB613900]
We report the development of a novel light-weight Al (520) alloy-based composite reinforced with particles of a Cu-based (Cu54Zr36Ti10) metallic glass by mechanical milling followed by induction heated sintering. The consolidation of the composite is performed at a temperature in the super-cooled liquid region of the metallic glass just above its glass-transition temperature (T-g). Metallic glasses are a promising alternative reinforcement material for metal-matrix composites capable of producing significant strengthening along with a friendly sintering behavior. The mechanical milling procedures were properly established to allow reduction of the size of the metallic glass particles and their uniform distribution in the matrix. Microstructural observation of the composite did not reveal any porosity. The interface between the glassy particles and the matrix remained free of such defects. The fully dense consolidated composite showed a drastic gain in specific yield strength under compression relative to the matrix alloy and appreciable plasticity at fracture. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据