COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 41, 期 9, 页码 1148-1155出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2010.04.013
关键词
Polymer-matrix composites (PMCs); Electrical properties; Powder processing
资金
- Council of Scientific and Industrial Research (CSIR, India)
- Department of Science and Technology, New Delhi
The present study investigates the dielectric and thermal properties of PTFE/Sm2Si2O7 composites. The composites were prepared by powder processing technique followed by hot pressing The variation of the dielectric properties with filler content (0-0.5 V-f) was studied at 1 MHz and 9 GHz The filler surface was chemically modified using phenyl trimethoxy silane (PTMS) as a coupling agent The microstructural study using scanning electron microscopy (SEM) showed that the particles were well dispersed in the matrix when coupled with PTMS. The surface modification led to an improvement in the dielectric properties The PTFE filled with 0.4 V-f silane treated Sm2Si2O7 composite showed a low dielectric loss of 0 0054 and slightly higher relative permittivity of 3.92 when compared with the untreated composite of the same composition. The experimental values of relative permittivities were compared with the theoretical predictions and the Effective Medium Theory was found to agree well even for higher content of silane treated filler It was found that the addition of silane coupling agent is very effective in improving the thermal properties of the PTFE/Sm2Si2O7 composites (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据