COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 39, 期 12, 页码 1924-1929出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2008.09.003
关键词
Neutralization; Ionomer; Nano-composites; Relaxation time
资金
- STAS Project
The highly neutralized ionorner-based nano-composite materials were prepared via direct melt processing using zinc oxide (as a neutralizating agent) and organically modified clay. The nano-structure was characterized using wide-angle X-ray diffraction analyses, transmission electron microscopy observations and rheometry. The dispersed organo-clay acted as catalytic sites for the neutralization. From TEM analyses, the nano-sized ionic aggregates with a domain size of approximately 2 run were randomly arranged in the ionomer matrix. The calculated aggregates density for the nano-composite was 0.08-0.15 nm(-2). The temperature-dependent relaxation process observed in the viscoelastic measurements was somehow affected by the presence of the silicate layers, whereas it was strongly affected by the specific interaction via ionic aggregated domains. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据