Transparent; Superhydrophobic; Silica nanocoating; Cetyltrimethoxylsilane
资金
- Jiangsu graduate students' research and innovation plans [CXLX12_0442]
- Nanjing University of Technology of China
Transparent superhydrophobic nanocoating, possessing a sub-100 nm roughness, a high water contact angle (>160 degrees) and a low sliding angle (<5 degrees), has been prepared by a simple sol-gel dip-coating method. The desired hierarchical sub-100 nm roughness, which renders the nanocoating transparency, was created by using 3-aminopropyltriethoxylsilane (APTEOS) as aggregated agent. Cetyltrimethoxylsilane (CTMS) was adopted as modifying agent subsequently to give the nanocoating superhydrophobicity. The influence of experiment parameters on the transparency and superhydrophobicity of as-prepared nanocoating were investigated herein to get the optimum preparing conditions. The obtained nanocoating before and after modification were characterized and confirmed by various technologies including Fourier transform infrared (FT-IR) spectroscopy, Si-29 CP (cross-polarization) MAS NMR, X-ray photoelectron spectroscopy (XPS), thermal analysis, atomic force microscopy (AFM) and transmission electron microscopy (TEM). The as-prepared transparent superhydrophobic nanocoating exhibits a good moisture resistance, and it could switch from superhydrophobic (>160 degrees) to superhydrophilic (0 degrees) after heat-treating at a temperature higher than 500 degrees C. Crown Copyright (C) 2013 Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据