期刊
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS
卷 388, 期 1-3, 页码 49-58出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.colsurfa.2011.08.007
关键词
Nanoparticles; Hexagonal boron nitride; Dispersion; Bead mill; Silane coupling agent
资金
- Ministry of Education, Culture, Sports, Science and Technology of Japan [22246099]
- Grants-in-Aid for Scientific Research [22246099, 23760729] Funding Source: KAKEN
This paper presents the surface functionalization with silane coupling agents for dispersing and stabilizing hexagonal boron nitride (hBN) nanoparticle suspension in a water phase. Fine milling using 30 mu m bead technology was utilized for the reduction of particle size, while dispersing agents with silane coupling agents were used for surface modification to enhance dispersion stability. A monodispersed hBN nanoparticle was obtained by controlling the processing parameters and by optimizing the dispersant dosage. The hBN nanoparticle suspension showed a high degree of dispersion stability with a zeta potential below -40 mV when (3-acryl-oxypropyl) trimethoxysilane (APMS) was used as the dispersing agent. Under optimal operation conditions for bead milling, the final average size of the particle distribution for the hBN suspension was 46 nm and 38 nm for 0.5 wt.% and 5 wt.% hBN, respectively. In addition, the surface characteristics, morphology, crystal structure and chemical composition of the hBN particles before and after bead milling were investigated to know the effect of bead milling. Finally, the surface functionalization mechanism that enhanced the stability of hBN nanoparticle dispersion by electrosteric stabilization was also proposed. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据