COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS
卷 339, 期 1-3, 页码 35-42出版社
ELSEVIER
DOI: 10.1016/j.colsurfa.2009.01.009
关键词
Magnetite; Nanoparticle; Surface-functionalization; Phosphonic acids; Stability
资金
- XPS
- CSIR New Delhi
This paper describes syntheses of stable functionalized iron oxide nanoparticles through surface modification of magnetic iron oxide nanoparticles with tailor-made phosphonic acids of type X(CH2)(n)PO3H (where X = -COOH, -NH2). Iron oxide nanoparticles were synthesized by co-precipitation method and the surface modification process was achieved using ultrasonic probe. XRD analysis shows that the crystalline structure of iron oxide nanoparticle remains unaffected even after surface modification with phosphonic acid-based coupling molecules. FTIR and XPS studies indicate that phosphonic acid binds on iron oxides preferably through tridentate bonding mode. TEM analysis shows narrow size distribution and uniform morphology of phosphonoacetic acid and 2-carboxyethyl phosphonic acid modified particles. BET surface area and phosphorous content analysis show higher coverage by -COOH terminated phosphonic acids than -NH2 terminated phosphonic acids in the particular reaction condition. DLS study shows almost no change in hydrodynamic diameter of phosphonoacetic acid and 2-carboxyethyl phosphonic acid modified particles in a wide pH range. (C) 2009 Elsevier B.V. All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据