COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS
卷 313, 期 -, 页码 415-418出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.colsurfa.2007.04.123
关键词
ammonium aluminum carbonate hydroxide (AACH); pH; alpha-Al2O3; nanopowders; TTT diagram
An alpha-Al2O3 nanopowder was prepared via the thermal decomposition of ammonium aluminum carbonate hydroxide (AACH). The AACH precursor, which had an average crystallite size of 5-8 nm, was fabricated at a reaction temperature of 8 degrees C with the pH of the aqueous ammonium hydrogen carbonate (AHC) precursor solution set to 10, which afforded the highest [NH4+][AlO(OH)(n)(SO4)(-)(3-n/2)]][HCO2-] ionic concentration. The AACH precursor was transformed to NH4Al(SO4)(2), rhombohedral (Al-2(SO4)(3)), amorphous-, theta-, and alpha-Al2O3 according to the heat-treatment temperature. A time-temperature-transformation (TTT) diagram for thermal decomposition in air was determined. The critical particle size of theta-Al2O3 in the theta -> alpha a phase transformation was similar to 30 nm. Homogeneous, spherical alpha-Al2O3 nanopowders with an average particle size of 70 nm were prepared by firing the precursor crystallites at 1150 degrees C for 3 h in air. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据