Electrodeposition of CdTe thin films using nitrate precursor for applications in solar cells

Cadmium telluride (CdTe) thin films have been electrodeposited (ED) on glass/fluorine-doped tin oxide (FTO) substrates using simplified two-electrode system in acidic and aqueous solution containing Cd(NO3)(2) 4H(2)O and TeO2. The X-ray diffraction (XRD), optical absorption, photoelectrochemical (PEC) cell measurements, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) have been carried out to study the structural, optical, electrical and morphological properties of the CdTe layers. The XRD study shows that the ED-CdTe layers are polycrystalline with cubic crystal structure. Results obtained from optical absorption reveal that the bandgaps of the as-deposited and the CdCl2 treated CdTe layers are in the ranges similar to 1.50 to similar to 1.54 eV and similar to 1.46 to similar to 1.51 eV, respectively. Observation from PEC measurements indicates a p-, i- and n-type electrical conductivity for as-deposited CdTe layers grown in the cathodic voltage range (1,247-1,258) mV. The SEM images indicate noticeable change in CdTe grain size from similar to 85 to similar to 430 nm after CdCl2 treatment with uniform surface coverage of the glass/FTO substrate. The TEM images show the columnar growth structure for as-deposited and CdCl2 treated CdTe layers. The TEM images also indicate an increase in grain's diameter from similar to 50 to similar to 200 nm after CdCl2 treatment.