期刊
JOURNAL OF MATERIALS RESEARCH
卷 30, 期 10, 页码 1661-1669出版社
CAMBRIDGE UNIV PRESS
DOI: 10.1557/jmr.2015.110
关键词
-
资金
- National High-Tech Program (863) of PR China [21100002013101006]
Heat-resistant Al-8.5Fe-1.3V-1.7Si (wt%) aluminum alloy components were fabricated using selective laser melting (SLM). The as-built samples were examined in terms of density, chemical composition, surface morphologies, microstructures, and mechanical behavior. The results show that nearly full dense samples with the relative density of 99.3% can be produced. The chemical composition of the deposited material is close to that of the powder, presenting a limited aluminum loss and a low oxygen pickup. The SLM specimens consist of three typical zones: the fusion zone (FZ), the remelting border zone (RBZ), and the heat-affected zone (HAZ). Ultrafine continuous cellular -Al networks are observed in the FZ. The HAZ exhibits fine rounded Al-12(Fe,V)(3)Si particles (10-70 nm) distributed homogeneously in the -Al matrix, while the rectangle-like AlmFe-type phase (m = 4.0-4.4) with 100-500 nm in size is preferably formed in the RBZ. The microhardness of the parts shows directional independent, with a mean value of 246 HV0.1.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据