Dilatometric studies of C-Mn hypoeutectoid steel with an as-cast structure were carried out to study the effects of the heating or cooling rate, heating and cooling process on phase transformation, and the thermal expansion coefficient. As the heating or cooling rate (V-c) increased, the characteristic temperatures of A(c1), A(cp), and A(c3) also rose, while A(r3), A(r1), and A(rp) fell. In addition, the phase transformation temperature range (A(c3)-A(c1)) rose, while (A(r3)-A(rp)) fell as the heating or cooling rate increased. At the same time, the maximum thermal expansion coefficients vertical bar alpha(T)vertical bar between the heating and cooling processes during phase transformation showed significant differences, and the difference (vertical bar Delta alpha(T)vertical bar) in the maximum vertical bar alpha(T)vertical bar between these processes increased along with the heating or cooling rate, and this is because of the different phase transformation rates, with regard to the change from austenite to ferrite on cooling and ferrite to austenite on heating. During the heating process, the phase transformation rate of ferrite to austenite first decreases and then increases as the temperature rises, and the phase transformation rate of austenite to ferrite first increases and then decreases during the cooling process. The evolution of carbon and substitutional alloying elements (Si and Mn) in austenite during heating and cooling is also analyzed in this work.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据