We submit the report on the structural and magnetic studies of Sn and Ti doped cobalt ferrite materials in comparison with the pure CoFe2O4. The XRD result confirms the inverse spinet crystallization of the samples with a space group of Fd-3m. The homogeneity and the stoichiometry of the samples were confirmed with the help of energy dispersive X-ray analysis (EDS). The Raman spectra gave the peaks corresponding to the tetrahedral and octahedral groups. In the case of Sn doping, the right shift of the peaks indicate the presence of massive Sn4+ ion. The effect of the doping of the diamagnetic ions (Ti4+ and Sn4+) is well seen from the reduction of saturation magnetization value from 80 emu/g to 66 emu/g and 61 emu/g respectively. Anisotropy constant (K-1) values of all the compounds were calculated employing law of approach method. Values of K-1 is found to be 2.16, 1.60 and 1.93 x 10(6) erg/cm(3) for pure Co ferrite, Sn doped and Ti doped Co ferriLes respectively. Saturation magnetostriction (As) value of pure Co ferrite, SR doped and Ti doped Co ferrites are -108 x 10(-6), 115 x 10(-6) and -182 x 10(-6) respectively. Considerable enhancement in saturation magnetostriction was observed in the Ti doped Co ferrite. The variation of d lambda/dH with applied magnetic field is seen to be less for all the samples, due to the larger crystalline anisotropy of Co2+ ions. (C) 2015 Elsevier B.V. All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据