M-type hexaferrites; XRD; FE-SEM; Magnetization
M type barium hexaferrites BaCexFe12-xO19 (0 <= x <= 0.3) (BCFO) were synthesized by the sol-gel auto combination method. Optimum annealing temperature of hexagonal phase was determined by using the TGA analysis. The annealing temperature form the TGA is 1000 degrees C samples annealed 1000 degrees C for 5 h to produce M type hexaferrites. X-ray diffraction data run to full Prof Program (Winploter 2010) pattern indicate that samples are single phase hexagonal structure with space group P6(3)/mmc Lattice parameter 'a' and 'c' increase with increase in Ce content x. Results of field emission scanning electron microscope show that the grains are regular hexagonal platelets with sizes from 0.3 to 1.4 mu m It is observed that from M-H curve value of the saturation magnetization and coercivity decreases with increasing x. Curie temperature from magnetization with temperature plot is found to decrease with Ce3+ substitution x due to decreases in magnetic interaction. (C) 2014 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据