JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 374, 期 -, 页码 18-21出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2014.08.002
关键词
Magnetic; Electrical; Hysteresis; XRD; Rhombohedral; Magneto crystalline anisotropy
资金
- Department of Science and Technology (DST) [SR/FTP/PS-161/2011]
We have examined the structural, magnetic and electrical properties of L2 and Mn co-substituted bismuth ferrite (BFO) samples prepared by the sol-gel technique. The XRD patterns confirm the formation of pure phase, rhombohedral structure in BM. Manganese gave rise to spontaneous magnetization along with the clarity of magnetic hysteresis attributed to the mismatch of two magnetic ions Fe/Mn. The coercivity decreases with co substitution due to decrease in magneto crystalline anisotropy. It is observed that real part of dielectric constant (epsilon') decreases with the increase in frequency. It is observed the modification in dielectric properties that may be due to La substitution which suppressed the transition of Fe3+ to Fe2+ ions, at room temperature. With La substitution in BFO there is an apparent increase in Ps, Pr and Ec values. In the case of the pristine sample BFOO, Ps reaches 0.043 mu C/cm(2) at the applied field (E) of 30 kV/cm with remnant polarization (Pr) 0.008 mu C/cm(2) and coercive field (Ec) 7.79 kV/cm. For the sample Bi050La0.25Fe0,95Mn0,05O3 (BFO6) Ps reaches 0.376 mu C/cm(2) at the applied field of 30 kV/cm with Pr 0.126 mu C/cm(2) and coercive field 10.3 kV/cm. (c) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据