期刊
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 373, 期 -, 页码 213-216出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2014.02.072
关键词
Iron oxide nanoparticle; Hydrothermal method; Co-precipitation
资金
- Balikesir University Research Grant [BAP 2012/37]
- State Planning Organization, Turkey [2005K120170]
Magnetic iron oxide nanoparticles with various sizes and magnetic properties were synthesized by using a hydrothermal method. The initial nanoparticles were obtained by co-precipitation of ferric and ferrous salts and then treated under a hydrothermal condition for 1-120 h at 160 degrees C. At reaction time of 12 h, further treatment on the particles was performed at 200 degrees C. The resultant nanoparticles were characterized by transmission electron microscopy (TEM), X-ray diffractometer (XRD) and vibrating sample magnetometer. The images obtained by TEM showed that the particles are around spherical in shape. The mean size of particles increased from 14 +/- 4 nm to 74 +/- 9 nm as the reaction time was increased from 1 h to 120 h. From the XRD patterns, high crystalline iron oxide nanoparticles were obtained with increasing reaction time and temperature. The saturation magnetizations obtained from magnetization curves were found to be rising from 74.9 to 93.5 emu/g that is consistent with the bulk value of the magnetite. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据