JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 389, 期 -, 页码 153-156出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2015.04.057
关键词
ZnO; Nanostructures; Magnetic properties; Crystal structure
资金
- Taif University, Saudi Arabia [2881-434-1]
- Bahcesehir University, Faculty of Engineering and Natural Sciences, Besiktas, Istanbul, Turkey
The doped ZnO system Zn0.95Cr0.05O (ZCO) was prepared as nano-polycrystalline by a simple sol-gel process and annealed at different temperatures. Structural and microstructure analyses are performed by applying x-ray diffraction (XRD) and Rietveld method. Results showed that Cr ions reside in the ZnO lattice substitutionally for Zn yielding ZCO single phase. The Rietveld refined u-fractional coordinate of Zn/Cr decreased with the annealing temperature from 0.3879 angstrom at 400 degrees C to 0.3740 angstrom at 600 degrees C. The Zn tetrahedrons become more symmetric and the distortion is gradually relieved by annealing. The field cooled (FC) and zero field cooled (ZFC) magnetization versus temperature and the magnetization versus applied field at different temperatures were carried out Measurements indicated that the absence of ferromagnetic behavior with magnetization slightly changed by changing the annealing temperature and no saturation. The Curie-Weiss paramagnetic temperature theta for annealed samples is negative indicating the antiferromagnetic nature of the samples. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据