JOURNAL OF LUMINESCENCE
卷 167, 期 -, 页码 327-332出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jlumin.2015.07.004
关键词
Ce3+; Dy3+; Zinc-sodium-aluminosilicate glasses; Photoluminescence; Radiative energy transfer; White light
类别
资金
- PROMEP [914057]
- CONACYT (Mexico)-CNR (Italy) [173855]
A spectroscopic investigation of 1% Dy2O3-singly doped and 0.5% Ce2O3-1.0% Dy2O3-codoped zinc-sodium-aluminosilicate glasses was performed by analyzing their absorption and photoluminescence spectra, and decay times. Warm white yellow light emission, with (0.419, 0.440) CIE1931 chromaticity coordinates and 3579 K color temperature, is obtained in the Dy3+-singly doped glass excited at 399 nm, which fits to the requirements of GaN LEDs. A quantum efficiency of 74% and a very high optical gain (38.7 x 10(-25) cm(-2) s) were estimated for the dysprosium F-4(9/2) level luminescence, which might also make the Dy3+-doped glass a promising gain medium for solid state yellow laser pumped by GaN LEDs. In the Ce3+/Dy3+-codoped glass a radiative energy transfer from Ce3+ to Dy3+ is observed upon LTV excitation (310-365 nm), with a Ce3+ to Dy3+ interaction distance that could be greater than 6-12 angstrom. The emission color from the codoped glass can be tuned with the excitation wavelength from blue light (0.247, 0.245), upon 310 nm excitation, to cold white light (0.284, 0300), with a 9052 K color temperature, upon 365 nm excitation. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据