bulk metallic glass; glass forming ability; mechanical properties; Co alloys
资金
- National Basic Research Program of China [2007CB613900]
- National Natural Science Foundation of China [51071008]
Co48-x Fe (x) Cr15Mo14C15B6Er2 (x = 2.5 and 5) bulk metallic glasses (BMGs) with critical size (d (c)) up to 15 mm in diameter were synthesized by copper mold casting. Co43Fe5Cr15Mo14C15B6Er2 BMG has a wide supercooled liquid region (84 K) and ultrahigh fracture strength exceeding 5000 MPa, which is the highest value for reported metallic glasses with d (c) exceeding 1 cm. Furthermore, the Poisson ratio, Young modulus, shear modulus and bulk modulus of this alloy were evaluated to be 0.31, 217 GPa, 82 GPa and 214 GPa, respectively. The ideal configurational entropy of Co48-x Fe (x) Cr15Mo14C15B6Er2 (x = 0 and 5) has been calculated. The introduction of the similar element Fe in the Fe-free Co-Cr-Mo-C-B-Er alloy will be beneficial to increasing the ideal configurational entropy and depressing the critical cooling rate to achieve greater glass-forming ability. The combination of superior glass-forming ability and ultrahigh fracture strength makes the present Co48-x Fe (x) Cr15Mo14C15B6Er2 (x = 2.5 and 5) BMGs promising candidates as advanced structural materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据