tetraethoxyorthosilicate; silica coating; hydrophobic effect; nanoparticles
资金
- Social Development Program of Jiangsu Province [BS2006050]
The conservation of historic sculptures is receiving growing attention because of the increasing air pollution. A hydrophobic silica coating was synthesized to protect historic sculptures from weathering by starting from a solution of tetraethoxyorthosilicate (TEOS) precursor using hexadecyltrimethoxysilane (HDTMS) as hydrophobic modifier in the presence of ammonia as a catalyst. The molar ratio of ethanol, TEOS, H2O and NH4OH was kept constant at 8 : 0.045 : 3 : 2.8 and the molar ratio of HDTMS/TEOS (M) was varied from 0 to 0.458. The organic modification was confirmed by infrared spectroscopic studies, and the hydrophobicity of the coating was tested by the contact angle measurements. The stone surface morphology of sample treated with silica coating was characterized. The results showed that the nanocomposites were composed of spherical particles with grain size of about 190 nm in diameter. After the limestone's surface was modified, the contact angle of limestone increased from 20 degrees to 100 degrees for M=0.458. The protective performance evaluated with its ability to resist acid rain reveals that the protective effects are satisfying.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据