期刊
CHEMPHYSCHEM
卷 14, 期 12, 页码 2793-2799出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/cphc.201300290
关键词
hydrothermal synthesis; nanostructures; optical properties; photovoltaics; semiconductors
资金
- University Grants Commission (UGC)-India
- Department of Science and Technology (DST) Innovation in Science Pursuit for Inspired Research (INSPIRE) program
- DST
- Board of Research in Nuclear Sciences, Department of Atomic Energy (BRNS-DAE) [2011/20/37P/11/BRNS/1733]
A simple, yet novel hydrothermal method has been developed to synthesize surfactant-free Cu2ZnSnS4 nanocrystal ink in water. The environmentally friendly, 2-4 nm ultrafine particles are stable in water for several weeks. Detailed X-ray diffraction (XRD) and high-resolution transmission electron microscopy revealed the formation of single-crystalline-kesterite-phase Cu2ZnSnS4. Elemental mapping by scanning electron microscopy/energy dispersive spectrometry corroborated the presence of all four elements in a stoichiometric ratio with minor sulfur deficiency. Finally, Raman spectroscopy ruled out the possible presence of impurities of ZnS, Cu2SnS3, SnS, SnS2, Cu2-xS, or Sn2S3, which often interfere with the XRD and optical spectra of Cu2ZnSnS4. X-ray photoelectron spectroscopic studies of the as-synthesized samples confirmed that the oxidation states of the four elements match those of the bulk sample. Optical absorption analyses of thin film and solution samples showed high absorption efficiency (>10(4) cm(-1)) across the visible and near-infrared spectral regions and a band gap E-g of 1.75 eV for the as-synthesized sample. A non-ohmic asymmetric rectifying response was observed in the I-V measurement at room temperature. The nonlinearity was more pronounced for this p-type semiconductor when the resistance was measured against temperature in the range 180-400 K, which was detected in the hot-point probe measurement.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据