CO2 adsorption; CO2 sequestration; X-zeolites; desilication; Cs-exchanged zeolites
Adsorption of carbon dioxide on alkaline modified X zeolites was investigated by temperature programmed desorption (TPD) analysis of these materials previously saturated with CO2 at 50, 100 and 200 degrees C. Parent X zeolite (in its sodium form) was treated with different sodium and cesium aqueous solutions, using both carbonates and hydroxides as precursors. The resulting materials were characterised by nitrogen physisorption, XRD, and NH3-TPD, in order to determine their morphological, crystallographic and chemical properties. Slight desilication phenomena were observed using hydroxides as precursors, whereas the treatment with Cs salts lead to higher crystallinity losses. Several successive adsorption-desorption cycles were carried out in order to check the regenerability of the adsorbents. Cesium-treated zeolites present higher carbon dioxide retention capacities than the sodium treated and than the parent material. When working with these Cs-modified materials, the desorption takes place mainly at temperatures between 250 and 400 degrees C, results of great practical interest, since it allows the use these kinds of materials for adsorption-desorption cycles. The evolution of the retention capacity with temperature is also markedly more positive for Cs-treated zeolite, especially when carbonate is used as the precursor. These materials maintain high retention capacities at 100 degrees C (10 mg g(-1)) and even at 200 degrees C (3 mg g(-1)), temperatures at which the most of the adsorbents are inactive. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据