CHEMISTRY-A EUROPEAN JOURNAL
卷 18, 期 17, 页码 5319-5324出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/chem.201102944
关键词
manganese; methylene blue; mesoporous materials; nanostructures; porosity
资金
- 973 Project of China [2011CB935901]
- National Nature Science Found of China
- Academy of Sciences [11179043]
- National Nature Science Fund of China [91022033, 20971079, 20871075]
- Independent Innovation Foundations of Shandong University [2009TS017, 2009 JC019, yzc10092]
Branched MnOOH nanorods with diameters in the range of 50150 nm and lengths of up to tens of micrometers were prepared by using potassium permanganate (KMnO4) and PEG 400 (PEG=polyethylene glycol) as starting materials through a simple hydrothermal process at 160 degrees C. After annealing at 300 degrees C under a N2 atmosphere for 5 h, MnOOH nanorods became gradually dehydrated and transformed into mesoporous Mn3O4 nanorods with a slight size-shrinking. The as-obtained mesoporous Mn3O4 nanorods had an average surface area of 32.88 m2?g-1 and a mean pore size of 3.7 nm. Through tuning the experimental parameters, such as the annealing atmosphere and temperature, beta-MnO2, Mn2O3, Mn3O4, MnO, and Mn5O8 were selectively produced. Among these structures, mesoporous Mn3O4 nanorods were efficient for the catalytic degradation of methylene blue (MB) in the presence of H2O2 at 80 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据