CHEMISTRY OF MATERIALS
卷 23, 期 8, 页码 2159-2165出版社
AMER CHEMICAL SOC
DOI: 10.1021/cm103661q
关键词
in situ high temperature XRD; PtCu3; alloy formation; particle growth; phase transformation; bimetallic catalyst
资金
- Geraete GmbH
- Bruker AXS
- DFG
Bimetallic alloy nanoparticles exhibit a complex, (for the most part) poorly understood, crystallographic phase behavior, rarely following their macroscopic counterparts. We have studied formation kinetics, time scales of individual processes, compositional changes, and particle growth rates of Pt bimetallic alloy nanoparticles. We chose the Pt-Cu system, because of its technological importance as a precursor for core shell nanoparticle electrocatalysts. We provide correlation of annealing control parameters, such as heating rate, temperature, and time, with microscopic alloy structure, composition, and particle size. We have clarified the roles of annealing temperature and time in the alloy formation process and traced out entire Vegard-type structure composition relationships over a wide temperature range. We have found that, during heating ramps, the annealing temperature essentially controls the Cu content of the resulting disordered Pt-Cu lattices. Increasing annealing times, in contrast, leads primarily to particle growth. Phase ordering occurs only during cooling. Our insight offers practical synthetic guidelines toward single-phase ordered and disordered PtCu3 alloy nanoparticles with optimized particle dispersion.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据