期刊
CHEMISTRY OF MATERIALS
卷 23, 期 11, 页码 2781-2785出版社
AMER CHEMICAL SOC
DOI: 10.1021/cm103600q
关键词
mesostructure; anatase; self-assembly; high-resolution electron diffraction; microemulsion; EISA
资金
- National Graduate School in Material Science and the Foundation for Strategic Research
- Swedish Research Council
- Grants-in-Aid for Scientific Research [23710132] Funding Source: KAKEN
A new direct synthesis methodology for the preparation of mesoporous titania with hexagonal mesostructure and with walls of tunable crystallinity and crystallite size has been developed. As the crystallites grow they eventually reach a point where they are too big to fit within the pore walls, the mesoorder becomes distorted and is finally lost. It is run at an unprecedented low temperature of 40 degrees C without the need for an autoclave or high-temperature post-treatment procedures and is thus compatible with low temperature stable substrates. High-resolution transmission electron microscopy and electron diffraction reveal that the pore walls of the mesoordered material consists of anatase TiO2 nanoparticles. The method allows for a wide choice of synthesis time during which the anatase crystallites grow slowly within the range of 2-5 nm in size but needs to be kept such that the crystallites have not yet grown too large for them to be coassembled into an ordered mesostructure.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据