期刊
CHEMISTRY OF MATERIALS
卷 22, 期 9, 页码 2790-2803出版社
AMER CHEMICAL SOC
DOI: 10.1021/cm903662a
关键词
-
资金
- National Science Foundation [CHE-0809562, CMMI-0653919]
- NSF [CHE-95-31247]
- NIH [1S10RR11962-01]
- Division Of Chemistry
- Direct For Mathematical & Physical Scien [0809562] Funding Source: National Science Foundation
SiC retains high mechanical strength and oxidation stability at temperatures above 1500 degrees C, representing a viable alternative to silica, alumina, and carbon, which have been in use as catalyst supports for more than 60 years. Preparation of monolithic porous SiC is usually elaborate and porosities around 30% v/v are typically considered high. This report describes the synthesis of monolithic highly porous (70% v/v) SiC by carbothermal reduction (1200-1600 degrees C) of 3D sol-gel silica nanostructures (aerogels) conformally coated and cross-linked with polyacrylonitrile (PAN). Synthesis of PAN-cross-linked silica aerogels is carried out in one pot by simple mixing of the monomers, whereas conversion to SiC is carried out in a tube reactor by programmed heating. Intermediates after aromatization (225 degrees C in air) and carbonization (800 degrees C under Ar) were isolated and characterized for their chemical composition and materials properties. Data are interpreted mechanistically and were used iteratively for process optimization. Solids Si-29 NMR validates use of skeletal densities (by He pycnometry) for the quantification of the conversion of silica to SiC. Consistent with the topology of the carbothermal process, data support complete conversion of SiO2, to SiC requiring a C:SiO2 ratio higher than the stoichiometric one (= 3). The morphology of the SiC network is invariant of the processing temperature between 1300 and 1600 degrees C, and hence it is advantageous to carry out the carbothemal process at higher temperatures where reactions run faster. Those samples are macroporous and consist of pure polycrystalline beta-SiC (skeletal density: 3.20 g cm(-3)) with surface areas in the range reported previously for biomorphic SiC (similar to 20 m(2) g(-1)). Although the micromorphology remains constant, the crystallite size of SiC increases with processing temperature (from 7.1 nm at 1300 degrees C to 16.5 nm at 1600 degrees C). Samples processed at 1200 C are mesoporous and amorphous (by XRD), even though they consist of similar to 75% mol/mol SiC. The change in the morphology of SiC in the 1200-1300 degrees C range has been explained by a melting mechanism. This comprises the first report of using a polymer crosslinked aerogel for the synthesis of another porous material.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据