The effects of annealing on the magnetic properties of nanocrystalline Ni1-xZnxFe2O4 (x = 0.2, 0.4) have been studied. The as-prepared x = 0.2 and 0.4 samples with the particle size of about 6 nm present a relatively low blocking temperature of about 47 and 53 K, respectively, as derived from the peak of the zero-field-cooled direct current (dc) Susceptibility measurements. The particle size significantly increases after annealing. Up to the annealing temperature of 800 degrees C, the blocking temperature is found to increase with increasing particle size, whereas the effective anisotropy constant exhibits a maximum for an annealing temperature of 400 degrees C. The latter effect is attributed to two antagonist contributions: the First one is related to the partial densification of the particles which introduces canting in the crystal interfaces while the second one is related to the size increase of the particles which reduces the surface anisotropy contribution.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据