Titania films were grown on BaTiO3 (BTO) substrates by pulsed laser deposition to create (001)(Anatase)parallel to(100)(BTO), (100)(Rutile)parallel to(111)(BTO), and (110)(Rutile)parallel to(110)(BTO) heterostructures. The photochemical reactivity was evaluated by observing the amount of silver reduced by each film under identical conditions. The thickest films (100 nm) had reactivities that varied with the phase of titania and the crystal orientation. Thin films (15 nm), on the other hand, had reactivities that were approximately the same. Furthermore, reaction products were spatially distributed in patterns consistent with the underlying domain structure of the substrate. For the case of (110)(Rutile)parallel to(110)(BTO), the thin films are more reactive than the thick films, showing that the dipolar Fields in the ferroelectrie substrate enhance the reactivity of (110) rutile.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据