期刊
JOURNAL OF POROUS MATERIALS
卷 8, 期 1, 页码 43-48出版社
KLUWER ACADEMIC PUBL
DOI: 10.1023/A:1026522401784
关键词
porous silica; activated carbon; porous properties; fixation; yeast
Mixtures of small silica particles and activated carbon were heated at 1250-1450 degreesC in an inert atmosphere to make nano- and macro-sized porous silica for incorporating yeast in the porous strucrure. Without activated carbon, porous silica of 45-60% porosity and 15-30 mum pore diameter was produced with a specific surface area below 1 m(2)/g. By the addition of 8 wt% of activated carbon granules, the surface area of porous silica increased to 100 m(2)/g at 1250 degreesC. It was confirmed that there were micropores(1.2 nm) and mesopores(4.0 nm) due to activated carbon granules in porous silica when granule type activated carbon was used. However, in the case of activated carbon fiber, its micro- and mesoporous structure was destroyed in the firing process. The fixation of Z. rouxii yeasts was promoted on the porous silica with activated carbon.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据