期刊
CERAMICS INTERNATIONAL
卷 40, 期 5, 页码 6807-6814出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2013.11.143
关键词
Al2O3; Ceria; Freeze-drying; CGO; Alumina
资金
- Spanish Government Research Program (FEDER funds) [MAT2007-60127, MAT2010-16007]
- AECI-through PCI-project [A/8026/07]
A freeze-drying precursor method was used to obtain submicrometric powders of ceria-based materials such as Ce1-xGdxO2-delta (x=0, 0.01, 0.05, 0.10 and 0.20), 80%CeO2-20%ZrO2, 80%CeO2-20%Al2O3 and (1-y)Ce0.99Gd0.01O2-delta-(y)Al2O3 (y=0.01, 0.02, 0.05, 0.10 and 0.30) at temperatures as low as 400 degrees C. The phase formation and evolution with the temperature was studied by X-ray diffraction (XRD). Also, temperature programmed reduction (TPR) was performed to investigate the reducibility of the ceramic powders. It was observed that after reduction of the ceria-based materials the fluorite structure of the samples was retained. The TPR profiles showed two peaks which are associated to the surface and bulk ceria reduction processes. Likewise, after the TPR measurements the resulting powders have showed high phase stability and reproducibility. XPS results confirmed the reduction of Ce4+ to (Ce3+ +Ce4+) ratio with alumina doping. (c) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据