(Ti,W,Nb)C solid solution was obtained via microwave-assisted carbothermal reduction (MWCR) which was more cost-effective and timesaving than conventional carbothermal reduction (CR). Oxide graphite mixtures were used as starting materials in the procedures. The phase evolution during MWCR has been discussed and compared with conventional CR in terms of the X-ray diffractometry. Microwave irradiation accelerated the formation of individual carbides (WC and NbC) as well as the formation of the final complete solid solution. The monolithic (Ti, W,Nb)C solid solution was synthesized at 1250 degrees C for 30 min. The agglomerates sizes of the final product were in the range of 100-350 nm. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据