To evaluate the impact sintering additives have on the processing and performance of 8 mol% yttria stabilized zirconia (8YSZ), the 25-1525 degrees C sintering kinetics, phase purity, microstructure, and electrical properties of a single batch of 8YSZ powder surface-coated with 1, 3 and 5 mol% of barium, bismuth, calcium, cobalt, copper, iron, lithium, magnesium, manganese, nickel, strontium or zinc were investigated via constant heating rate dilatometry, X-ray diffraction, scanning electron microscopy, and AC impedance spectroscopy. For electrochemical applications where dense 8YSZ is required, iron was found to give the best combination of 8YSZ cubic zirconia phase stability, high oxygen ion conductivity, and enhanced densification kinetics. 5 mol% iron was found to reduce the 8YSZ sintering temperature by similar to 150 degrees C. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据