Molybdenum trioxide (MoO3) thin films have been prepared by the spray pyrolysis technique on glass substrates at 460 degrees C using (NH4)(6)Mo7O24 center dot 4H(2)O (ACROS pure more than 99.0%) as precursor in the starting solution. X-ray analysis shows that MoO3 thin film crystallizes in orthorhombic structure with a preferred orientation of the crystallites along (020) and (040) directions. The surface topography of these films was performed by atomic force microscopy and the optical properties were investigated through reflectance and transmittance measurements. The optical band gap energy value is about 3.46 eV and the Urbach energy is of the order of 191 meV. Raman spectroscopy shows the bands' positions corresponding to alpha-MoO3 phase. PL measurements show two large bands located at 375 nm and 575 nm respectively. Finally, the electric conductivity of MoO3 thin film was investigated using impedance spectroscopy technique in the frequency range 5 Hz-13 MHz at various temperatures (300-500 degrees C). The variation of the conductivity in terms of the temperature is characterized by the existence of two ranges with activation energy of 1.00, and 0.42 eV. AC conductivity of MoO3 thin films is investigated through Jonsher law. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据