Zirconium compounds; Cermet; Reactive hot pressing; Densification behaviour; Microstructure
资金
- Japan Society for the Promotion of Science (JSPS) [25420722]
- Grants-in-Aid for Scientific Research [25420722] Funding Source: KAKEN
In this study, two methods of powder reactions and reactive hot-pressing were used for the reaction of Zr+B4C powder mixtures. The powder reactions were performed at various temperatures, between 600 degrees C and 1100 degrees C, to examine the reaction behaviour occurring during the synthesis. To fabricate a cermet composed of platelet-like ZrB2 grains and equiaxed ZrCx grains, with intergranular Zr phase, reactive hot-pressing was conduced within temperature range of 1100-1900 degrees C. The effects of temperature on the reactions, densification behaviour and microstructure of the samples were assessed. For samples sintered at 900 degrees C or above, the Zr+B4C mixture was converted into ZrB2 and ZrCx; the conversion was completed at similar to 1100 degrees C. Densification resulted from volume contraction due to the conversion of Zr+B4C mixture into ZrB2 and ZrCx, and the shrinkage due to grain boundary diffusion and grain boundary migration. For Zr+B4C mixtures sintered at or above 1400 degrees C, relative densities exceeding 97% were obtained. When sintered at or below 1400 degrees C, the resulting ZrB2-ZrCx-Zr cermet consisted of rod-like ZrB2 grains, equiaxed ZrCx grains and residual Zr. Highly-developed platelet-like ZrB2-ZrCx-Zr cermet was obtained only at sintering temperature of 1600 degrees C or greater. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据