Composite materials based on 8 wt% yttria partially stabilized zirconia, with additions of gadolinium zirconate, lanthanum lithium hexaaluminate, yttrium aluminum garnet and strontium zirconate were characterized. Samples were fabricated by hot-press sintering at 1550 degrees C. The effect of the secondary phase content on the mechanical properties of the composites was evaluated. Hardness, elastic modulus and fracture toughness of the fabricated composites were determined by means of depth-sensitive indentation testing. The fracture toughness of the samples as determined by the indentation method was found to increase with increasing YSZ content, reaching 3MPa.m(0.5) for samples with 80 wt% YSZ. The fracture toughness appeared to be affected by thermal expansion coefficient mismatch, crack bridging and crack deflection. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据