CERAMICS INTERNATIONAL
卷 39, 期 2, 页码 1651-1658出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.08.007
关键词
Milling; X-ray methods; Apatite; Nanostructures
资金
- Isfahan University of Technology
The aim of this work was preparation and characterization of Mg-substituted nanostructured FA powders. Mg-substituted nanostructured FA powders were synthesized with a chemical composition of Ca10-xMgx(PO4)(6)F-2, with x=0, 0.5, 1, 1.5 and 2 by mechanical alloying method. Successful substitution of Ca2+ with Mg ions in the fluorapatite lattice was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy (FTIR). The results showed that after 12 h of milling, pure nanocrystalline Mg-substituted FA powders with different Mg contents were synthesized. The incorporation of Mg ions into the fluorapatite caused the decrease of the lattice parameters. With increasing Mg content, the crystallinity of powder decreased while the degree of agglomeration of powder increased. SEM and TEM analysis showed that the powder was agglomerated and composed of nanocrystalline particles with the average particle size of less than 100 nm. (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据