CERAMICS INTERNATIONAL
卷 39, 期 7, 页码 7831-7838出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2013.03.043
关键词
Pseudo-capacitance; Sol-gel; Specific capacitance; Manganese acetate; Iron acetate
资金
- National Science Council of Taiwan
- National United University
Manganese oxide electrodes possessing pseudo-capacitance behaviors were successfully made with a simple sol-gel method. The experimental results showed that the specific capacitance was 101.2 F/g for pure manganese oxide films after annealing at 300 degrees C. However, the specific capacitance increased to 232.3 Fig with iron acetate (1.0 mol% Fe) addition and after annealing at 350 degrees C. The surface morphology observations revealed that the annealing temperature of 350 degrees C produced a higher surface area film with smaller pores. X-ray diffraction results showed that the manganese-iron oxide was composed of Mn3O4 and Mn2O3 phases, without iron oxide diffraction peaks. The manganese-iron oxide electrode with Mn3O4 and Mn2O3 phases exhibited good electrochemical performance and capacitance efficiency. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据