期刊
CERAMICS INTERNATIONAL
卷 39, 期 3, 页码 2423-2430出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.09.002
关键词
Porosity; Glass; Waste treatment; Sodium hydroxide
资金
- Capes
- CNPq [558595/2008-1]
- Finep [3903/06]
Glass foams using float glass waste and sodium hydroxide were produced. The influence of the sodium hydroxide amount in the foam formulation was studied. Titanium dioxide was used as a strengthening agent. The variations of temperature, heating rate and sintering time were investigated during the synthesis process. Open porosity was estimated using mercury porosimetry. The morphology of the glass foams was evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foams with macroporosity were obtained. Since the glass foams used glass waste as reactant, the results suggest the development of an alternative route for glass recycling. (c) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据