期刊
CERAMICS INTERNATIONAL
卷 39, 期 1, 页码 813-818出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.07.002
关键词
ZnO; Hydrothermal synthesis; Morphology; Photoluminescence
In the present work, well-dispersed two new structures of scale- and spindle-like ZnO were successfully. synthesized by using zinc nitrate hexahydrate as the starting material and also the low temperature hydrothermal process and any additional surfactant, organic solvents or catalytic agents The ZnO structures were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). Optical property of the ZnO structures was investigated by room-temperature photoluminescence (PL) spectroscopy. The results revealed that ZnO powders have hexagonal (wurtzite-type) crystal structure and a large amount of well-dispersed ZnO scale- and spindle-like structures was formed. The thickness of scales was in the range 40-60 nm and the diameter of spindles was in the range 50-70 nm. Room-temperature PL spectra from the ZnO structures showed a weak UV emission peak at similar to 382 nm and a very strong visible green emission at similar to 530 nm, that was ascribed to the transition between VoZni and valence band. (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据