期刊
CERAMICS INTERNATIONAL
卷 39, 期 6, 页码 6057-6062出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2013.01.022
关键词
Films; Electrical properties; Ferroelectric properties; Perovskites
资金
- Priority Research Centers Program through the National Research Foundation of Korea (NRF)
- Ministry of Education, Science and Technology [2010-0029634]
Pure BiFeO3 and rare earth and transition metal ions co-doped (Bi0.9Dy0.1)(Fe0.975TM0.025)O-3 (+/-) (delta) (TM=Ni2+, Cr3+ and Ti4+) thin films were prepared on Pt(111)/Ti/SiO2/Si(100) substrates by using a chemical solution deposition method. The changes in the microstructure and the electrical properties with doping elements were investigated. The thin films were well crystallized and randomly oriented, with no detectable impurity and secondary phases. The leakage current densities were reduced and the ferroelectric properties were improved in the co-doped thin films. Among the thin films, the (Bi0.9Dy0.1)(Fe0.975TM0.025)O-3 thin film exhibited well saturated hysteresis loops with remnant polarization (2P(r)) of 36 mu C/cm(2) and coercive electric field (2E(c)) of 954 kV/cm at 1000 kV/cm and low leakage current density of 1.91 x 10(-5) A/cm(2) at 100 kV/cm. The enhanced properties observed in the co-doped thin films could be considered as being the result of the suppression of oxygen vacancies and of the modified microstructure. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据