卷 38, 期 8, 页码 6399-6404出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.05.012
关键词
Agglomerate; Mechanical alloying; SiBCN powder; TG-DTA-MS-IR
资金
- National Natural Science Foundation of China [51072041, 50902031, 51021002]
A powder mixture of cubic silicon, hexagonal boron nitride and graphite, with the molar ratio of Si:BN:C=2:1:3, was high-energy ball milled for 40 h, under argon atmosphere. The physical and surface characteristics, the microstructures and the behavior on heating of the as-milled SiBCN powder were carefully studied by SEM, nitrogen adsorption-desorption isotherms, XPS, FT-IR, XRD, TEM and thermogravimetry-differential thermal analysis-mass spectrometry-infrared spectroscopy (TG-DTA-MS-IR). Results show that the as-milled powder is amorphous and mainly consists of near-spherical agglomerates, 6.6 +/- 5.3 mu m in size deriving from the hard agglomeration of nano-primary particles. The specific surface area, the specific pore volume and the average pore diameter of the powder are 24.5 m(2)/g, 0.136207 cm(3)/g and 20.3 nm, respectively. The as-milled powder adsorbs water vapor, CO and CO2, and it is easy to oxidize. When heated in helium atmosphere, the powder desorbs water vapor, CO and CO2 at lower temperature, and rapidly degasifies CO and CO2 at temperatures approximately between 1350 degrees C and 1500 degrees C. (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据